QAMAR RESIN PROPERTIES

Item Grade HB18N FC21HS FC21HN FC20H FC18N FD21HS FD21HN FD18N CD18N
Test Method Unit
MI ISO 1872-2 g/10min 0.5 1.0 1.0 1.0 1.0 2.0 2.0 2.0 2.8
Density ASTM D4883 g/cm³ 0.918 0.918 0.918 0.918 0.918 0.918 0.918 0.918 0.918
Tensile Stress at Yield ISO 1872-2 MPa 9 9 9 9 9 9 9 9 9
Nominal Tensile Strain at Break ISO 1872-2 % >430 >430 >430 >430 >430 >430 >430 >430 >430
Flexural Modulus ISO 1872-2 MPa 200 200 200 200 200 200 200 200 200
Durometer Hardness (type D) ISO 868 55 55 55 55 55 54 54 54 54
Brittleness Temperature ISO 974 ºC <-70 <-70 <-70 <-70 <-70 <-70 <-70 <-70 <-70
Melting Point ISO 11357-3 ºC 122 122 122 122 122 122 122 122 122
Vicat Softening Temperature ISO 306 ºC 102 102 102 102 102 100 100 100 99
Anti-Blocking Agent/ Slip Agent
Characteristics High Strength High Clarity Standard Clarity Higher Clarity Easy to Extrude Basic Material High Clarity Standard Clarity Basic Material High Flow
Application Heavy Duty Bag General Purpose Blown Film for Customer-made Additive Formulation General Purpose Blown Film for Customer -made Additive Formulation Cast Film

QAMAR FILM PROPERTIES

Item Grade HB18N FC21HS FC21HN FC20H FC18N FD21HS FD21HN FD18N CD18N
Test Method Unit
MI ISO 1872-2 g/10min 0.5 1.0 1.0 1.0 1.0 2.0 2.0 2.0 2.8
Density ASTM D4883 g/cm³ 0.918 0.918 0.918 0.918 0.918 0.918 0.918 0.918 0.918
Film Thickness µm 30 30 30 30 30 30 30 30 30
Haze ISO 14782 % 7 8 11 6 8 11 14 11 12
Dart Drop Impact ISO 7765 g 130 120 120 110 120 110 110 110 100
Tensile Stress at Break MD ISO 527-3 MPa 60 55 55 45 55 40 40 40 35
TD 45 40 40 35 40 35 35 35 30
Nominal Tensile Strain at Break MD ISO 527-3 % 500 550 550 500 550 600 600 600 600
TD 850 850 850 800 850 900 900 900 900
Modulus of Elasticity in Tension MD ISO 527-3 MPa 200 190 190 200 190 190 190 190 190
TD 230 220 220 230 220 210 210 210 210
Elmendorf Tear Strength MD ISO 6383-2 N/mm 30 30 30 20 30 30 30 30 30
TD 170 160 160 160 160 140 140 140 120
Processing Conditions Resin Temperature 200ºC 180ºC
Blow up Ratio 2.0
Extruder 40mm, L/D=24
Die Diameter 75mm

Values in this Table represent typical laboratory average.