Polyethylene|SPDC LTD.

QAMAR is a brandname of LLDPE (butene type) produced by Eastern Petrochemical Company "SHARQ" using Unipol process and solely marketed through SPDC LTD.

【QAMAR GRADE MAP】

Characteristics	MI=0.5	MI=1	MI=2	MI=2.8
Standard Clarity	-	FC21HN	FD21HN	-
High Clarity	-	FC21HS	FD21HS	-
LDPE blended	-	FC20H	-	-
Non-Slip & Non-Antiblocking Agent	HB18N	FC18N	FD18N	CD18N

QAMAR-HD is a brandname of HDPE (butene type) produced by Eastern Petrochemical Company "SHARQ" using Unipol process and solely marketed through SPDC LTD.

QAMAR RESIN PROPERTIES
QAMARD FILM PROPERTIES

【QAMAR-HD RESIN PROPERTIES】

Item	Grade		F1
Item	Test Method	Unit	F1
MI*1	ISO 1872-2	g/10min	0.05
HLMI*2	ISO 1872-2	g/10min	9
Density	ISO 1872-2	g/cm³	0.952
Melting Point	ISO 11357-3	ºC	132
Vicat Softening Temperature	ISO 306	ºC	125
Additives			Antioxidants
Recommended Processing Method			Blown Film Fabrication
Applications			Grocery Sacks Shopping Bags
Processing Characteristics			Stability
Film Characteristics			Stiffness Strength

(Values in this table represent typical laboratory averages.)

*1 Melt Index(2.16kg)
*2 High Load Melt Index (21.6kg)

【QAMAR-HD FILM PROPERTIES】

Item		Grade		F1
Item		Test Method	Unit	F1
MI*1		ISO 1872-2	g/10min	0.05
HLMI*2		ISO 1872-2	g/10min	9
Density		ISO 1872-2	g/cm³	0.952
Film Tickness		-	µm	20
Haze		ISO 14782	%	50
Dart Drop Impact		ISO 7765	g	150
Tensile Stress at Break	MD	ISO 527-3	MPa	60
Tensile Stress at Break	TD	ISO 527-3	MPa	55
Nominal Tenslle Strain at Break	MD	ISO 527-3	%	270
Nominal Tenslle Strain at Break	TD	ISO 527-3	%	610
Modulus of Elasticity in Tension	MD	ISO 527-3	MPa	1,350
Modulus of Elasticity in Tension	TD	ISO 527-3	MPa	1,550
Elmendorf Tear Strength	MD	ISO 6383-2	N/mm	5
Elmendorf Tear Strength	TD	ISO 6383-2	N/mm	35
Processing Conditions		Resin Temparature		200ºC
		Blow up Ratio		3
		Extruder		50mm L/D=28
		Air Ring		SINGLE SLIT
		Die		100mm LIP GAP=1mm
		Output		60kg/h
		Take off Speed		60m/min

*1 Melt Index(2.16kg)
*2 High Load Melting Index (21.6kg)